| 产品特性：高流动 | 是否进口：否 | 产地：荷兰 |
| 厂家(产地)：荷兰 | 牌号：46HF4540 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PA46塑胶原料 | 加工级别：注塑级 |
| 特性级别：热稳定性、 标准级、 高流动 | 用途级别：电子电器部件、 家电部件 | 品牌：荷兰 |
| 产品规格：高流动 |
现货供应46HF4540高流动热稳定PA46塑胶原料，含40%玻璃纤维强化，高流动性，润滑，电子电气应用。
PA46 46HF4540物性表：
| Product Description | |
40% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications | |
| General | |
Material Status |
|
Availability | Africa & Middle EastAsia PacificEuropeLatin AmericaNorth America |
Filler / Reinforcement |
|
Additive |
|
Features | Heat StabilizedHigh Flow |
Uses |
|
Processing Method |
|
Resin ID |
|
| ASTM & *** Properties 1 | ||||
| Physical | Dry | Conditioned | Unit | Test Method |
Density | 1.51 | -- | g/cm? | *** 1183 |
Spiral Flow | ||||
-- 2 | 9.00 | -- | cm | |
-- 3 | 11.5 | -- | cm | |
-- 4 | 13.0 | -- | cm | |
Molding Shrinkage | *** 294-4 | |||
Across Flow | 1.1 | -- | % | |
Flow | 0.50 | -- | % | |
Water Absorption (Saturation, 23°C) | 8.1 | -- | % | *** 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) | 2.2 | -- | % | *** 62 |
Viscosity Number | 80.0 | -- | cm?/g | *** 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | *** 527-1 | |||
-- | 13000 | 8000 | MPa | |
120°C | 7000 | -- | MPa | |
160°C | 6000 | -- | MPa | |
Tensile Stress | *** 527-2 | |||
Break | 210 | 140 | MPa | |
Break, 120°C | 130 | -- | MPa | |
Break, 160°C | 115 | -- | MPa | |
Tensile Strain | *** 527-2 | |||
Break | 2.5 | 4.5 | % | |
Break, 120°C | 4.0 | -- | % | |
Break, 160°C | 4.0 | -- | % | |
Flexural Modulus | 12000 | 7000 | MPa | *** 178 |
Flexural Stress | 320 | 220 | MPa | *** 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | |||
-30°C | 12 | 12 | kJ/m? | |
23°C | 12 | 15 | kJ/m? | |
Charpy Unnotched Impact Strength | *** 179/1eU | |||
-30°C | 60 | 60 | kJ/m? | |
23°C | 70 | 95 | kJ/m? | |
| Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 290 | -- | °C | *** 75-2/B |
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 290 | -- | °C | *** 75-2/A |
Glass Transition Temperature 5 | 75.0 | -- | °C | *** 11357-2 |
Vicat Softening Temperature | 290 | -- | °C | *** 306/B50 |
Melting Temperature 5 | 295 | -- | °C | *** 11357-3 |
CLTE - Flow | 4.0E-5 | -- | cm/cm/°C | ASTM D696 |
CLTE - Flow | 1.5E-5 | -- | cm/cm/°C | *** 11359-2 |
CLTE - Transverse | 6.0E-5 | -- | cm/cm/°C | ASTM D696 |
CLTE - Transverse | 1.4E-4 | -- | cm/cm/°C | *** 11359-2 |
RTI Elec | UL 746B | |||
0.75 mm | 65.0 | -- | °C | |
3.0 mm | 65.0 | -- | °C | |
RTI Imp | UL 746B | |||
0.75 mm | 65.0 | -- | °C | |
3.0 mm | 65.0 | -- | °C | |
RTI Str | UL 746B | |||
0.75 mm | 65.0 | -- | °C | |
3.0 mm | 65.0 | -- | °C | |
| Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | -- | 1.0E+14 | ohms | IEC 62631-3-2 |
Volume Resistivity | 1.0E+13 | 1.0E+9 | ohms·m | IEC 62631-3-1 |
Electric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
Relative Permittivity | ||||
1.00 GHz | 3.60 | -- | IEC 61189-2-721 | |
1 MHz | 4.00 | 4.60 | IEC 62631-2-1 | |
100 Hz | 4.40 | 12.0 | IEC 62631-2-1 | |
Dissipation Factor | ||||
100 Hz | 8.0E-3 | 1500 | IEC 62631-2-1 | |
1 MHz | 0.023 | 900 | IEC 62631-2-1 | |
1.00 GHz | 0.030 | -- | IEC 61189-2-721 | |
Comparative Tracking Index | 475 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
Flame Rating | UL 94 | |||
1.5 mm | HB | -- | ||
3.0 mm | HB | -- | ||
Flammability Classification | IEC 60695-11-10, -20 | |||
1.5 mm | HB | -- | ||
3.0 mm | HB | -- |