供应基础创新塑料PX1005X高流动无卤阻燃PPO原料，高流动无卤阻燃。
基础创新塑料Noryl PX1005X物性：
| Physical | Nominal Value | Unit | Test Method |
Specific Gravity | 1.12 | g/cm? | ASTM D792 |
Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 37 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 37.0 | cm?/10min | *** 1133 |
Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
Molding Shrinkage - Across Flow 2 | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus 3 | 2400 | MPa | ASTM D638 |
Tensile Modulus | 2460 | MPa | *** 527-2/1 |
Tensile Strength 4 (Yield) | 55.2 | MPa | ASTM D638 |
Tensile Stress (Yield) | 53.8 | MPa | *** 527-2/50 |
Tensile Strength 4 (Break) | 41.4 | MPa | ASTM D638 |
Tensile Stress (Break) | 43.4 | MPa | *** 527-2/50 |
Tensile Elongation 4 (Yield) | 3.1 | % | ASTM D638 |
Tensile Strain (Yield) | 2.8 | % | *** 527-2/50 |
Tensile Elongation 4 (Break) | 17 | % | ASTM D638 |
Tensile Strain (Break) | 13 | % | *** 527-2/50 |
Flexural Modulus | ASTM D790 | ||
-- | 2430 | MPa | |
100 mm Span 5 | 2210 | MPa | |
Flexural Modulus 6 | 2480 | MPa | *** 178 |
Flexural Strength 6, 7 | 76.7 | MPa | *** 178 |
Flexural Strength | ASTM D790 | ||
Yield, 50.0 mm Span 8 | 80.0 | MPa | |
Yield, 100 mm Span 5 | 80.0 | MPa | |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength 9 (23°C) | 24 | kJ/m? | *** 179/1eA |
Notched Izod Impact | ASTM D256 | ||
-30°C | 91 | J/m | |
23°C | 300 | J/m | |
Notched Izod Impact Strength 10 (23°C) | 23 | kJ/m? | *** 180/1A |
Unnotched Izod Impact (23°C) | 1200 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, Unannealed, 3.20 mm | 84.4 | °C | |
0.45 MPa, Unannealed, 6.40 mm | 88.9 | °C | |
Heat Deflection Temperature 11 (0.45 MPa, Unannealed, 100 mm Span) | 88.2 | °C | *** 75-2/Be |
Deflection Temperature Under Load | ASTM D648 | ||
1.8 MPa, Unannealed, 3.20 mm | 72.8 | °C | |
1.8 MPa, Unannealed, 6.40 mm | 78.3 | °C | |
Heat Deflection Temperature 11 (1.8 MPa, Unannealed, 100 mm Span) | 75.6 | °C | *** 75-2/Ae |
Vicat Softening Temperature | 107 | °C | ASTM D1525 12 |
Vicat Softening Temperature | |||
-- | 94.0 | °C | *** 306/B50 |
-- | 97.0 | °C | *** 306/B120 |
CLTE - Flow (-40 to 40°C) | 0.000089 | cm/cm/°C | ASTM E831 |
CLTE - Transverse (-40 to 40°C) | 0.00010 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | > 1.0E+16 | ohm | ASTM D257 |
Volume Resistivity | 3.3E+16 | ohm·cm | ASTM D257 |
Dielectric Strength (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
Dielectric Constant | ASTM D150 | ||
50 Hz | 2.67 | ||
60 Hz | 2.67 | ||
1 MHz | 2.53 | ||
Dissipation Factor | ASTM D150 | ||
50 Hz | 0.012 | ||
60 Hz | 0.012 | ||
1 MHz | 0.0026 | ||
Arc Resistance (PLC) 13 | PLC 7 | ASTM D495 | |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating - UL | UL 94 | ||
1.02 mm | HB | ||
1.47 mm | V-0 | ||
3.00 mm | 5VA |
订购说明
★公司秉承“以诚为本，信誉至上”的经营宗旨，【诚信***】【服务***】【品质***】创立了自己的经营理念，在客户群树立了良好的***。为您提供充足的货源和专业的技术支持！公司所售之新料均***原厂原包，货真价实!
★公司货源充足，品种齐全，价格合理,量大从优,原厂原包,当天订货当天发货。我公司可以提供原料出厂报告(COA)，认证报告;UL认证、FDA认证、材质证明、***，ASTM物性资料、ROHS(SGS)报告、物质安全资料表(MSDS)物性、报价、UL报告、RoSH标准、SGS检测报告等）......
★支持物流，快递和货运; 支持现金，银行转账（广东省内可快递代收）.
★原料到厂后，请不要拆外包装，应先仔细检查原料的外包装是否完好及原料型号是否与您所订购原料型号相匹配。
★货物送达后，请***时间检查，发现物流过程中出现大量包装损坏及原料外漏的,请让物流人员出具证明并保存，并在24小时内与东莞佳唯斯塑胶原料有限公司颜小姐联系。
★如发货后未能及时收到，请及时与东莞佳唯斯塑胶原料有限公司颜小姐联系15382847379
★订购说明：自接到订单24小时内发货，广州市 深圳市 珠海市 汕头市 韶关市 河源市 梅州市 惠州市 汕尾市 东莞市 中山市 江门市 佛山市 阳江市 湛江市 茂名市 肇庆市 清远市 潮州市 揭阳市 云浮市等地区送货上门，广东省以外等地区协商物流配送，一次购买数量1000kg以上价格从优，欢迎各界朋友前来订购。
★我们的宗旨：【以优惠的价格给广大客户提供优质的品质。本公司货源充足，品种齐全，价格合理】