| 牌号：B30S | 产商/产地：德国/无锡 | 含量≥：99％ |
| 品牌：朗盛 | 纯度：99% | 密度：1.14kg/m3 |
| 用途：标准注塑级 | CAS：32131-17-2 |
供应德国朗盛B30S标准注塑级尼龙6塑胶原料，标准注射级，易流动，成型周期短，易脱摸，快速固化，宜制通用制品。
德国朗盛Durethan B30S物性物性：
| Physical | Dry | Conditioned | Unit | Test Method |
Specific Gravity | 1.14 | -- | g/cm? | ASTM D792 |
Density | 1.14 | -- | g/cm? | *** 1183 |
Apparent Density | 0.70 | -- | g/cm? | *** 60 |
Molding Shrinkage | *** 2577 | |||
Across Flow: 260°C, 3.00 mm 2 | 1.2 | -- | % | |
Across Flow: 120°C, 4 hr, 3.00 mm 3 | 0.40 | -- | % | |
Flow: 260°C, 3.00 mm 2 | 1.0 | -- | % | |
Flow: 120°C, 4 hr, 3.00 mm 3 | 0.32 | -- | % | |
Water Absorption (Saturation, 23°C) | 10 | -- | % | *** 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) | 3.0 | -- | % | *** 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus 4 (23°C) | 3200 | 1100 | MPa | ASTM D638 |
Tensile Modulus (23°C) | 3200 | 1000 | MPa | *** 527-2/1 |
Tensile Strength (Yield, 23°C) | 80.0 | 40.0 | MPa | ASTM D638 |
Tensile Stress (Yield, 23°C) | 80.0 | 40.0 | MPa | *** 527-2/50 |
Tensile Strength (Break, 23°C) | 50.0 | 60.0 | MPa | ASTM D638 |
Tensile Elongation (Yield, 23°C) | 4.0 | 20 | % | ASTM D638 |
Tensile Strain (Yield, 23°C) | 4.0 | 20 | % | *** 527-2/50 |
Tensile Elongation (Break, 23°C) | 35 | > 50 | % | ASTM D1708 |
Nominal Tensile Strain at Break (23°C) | 20 | > 50 | % | *** 527-2/50 |
Tensile Creep Modulus (1 hr) | -- | 800 | MPa | *** 899-1 |
Tensile Creep Modulus (1000 hr) | -- | 600 | MPa | *** 899-1 |
Flexural Modulus (23°C) | 2700 | 703 | MPa | ASTM D790 |
Flexural Modulus 5 (23°C) | 2900 | 850 | MPa | *** 178 |
Flexural Strength (5.0% Strain, 23°C) | 115 | 35.0 | MPa | ASTM D790 |
Flexural Strength 5 | *** 178 | |||
3.5% Strain, 23°C | 95.0 | 25.0 | MPa | |
23°C | 110 | 35.0 | MPa | |
Flexural Strain at Flexural Strength 6 (23°C) | 6.0 | 8.0 | % | *** 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | |||
-30°C | <10 | <10 | kJ/m? | |
23°C | <10 | 20 | kJ/m? | |
Charpy Unnotched Impact Strength | *** 179/1eU | |||
-30°C | No Break | No Break | ||
23°C | No Break | No Break | ||
Notched Izod Impact (23°C, 3.18 mm) | 59 | 750 | J/m | ASTM D256 |
Notched Izod Impact Strength (23°C) | <10 | <10 | kJ/m? | *** 180/1A |
Unnotched Izod Impact Strength | *** 180/1U | |||
-30°C | No Break | No Break | ||
23°C | No Break | No Break | ||
Multi-Axial Instrumented Impact Energy | *** 6603-2 | |||
-30°C | 10.0 | -- | J | |
23°C | 12.0 | -- | J | |
Multi-Axial Instrumented Impact Peak Force | *** 6603-2 | |||
-30°C | 6540 | -- | N | |
23°C | 5140 | -- | N | |
| Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness | 140 | 50.0 | MPa | *** 2039-1 |
| Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.99 mm) | 180 | -- | °C | ASTM D648 |
Heat Deflection Temperature (0.45 MPa, Unannealed) | 160 | -- | °C | *** 75-2/B |
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.99 mm) | 60.0 | -- | °C | ASTM D648 |
Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | -- | °C | *** 75-2/A |
Heat Deflection Temperature (8.0 MPa, Unannealed) | 45.0 | -- | °C | *** 75-2/C |
Vicat Softening Temperature | ||||
-- | 200 | -- | °C | *** 306/B50 |
-- | 200 | -- | °C | *** 306/B120 |
Melting Temperature | 222 | -- | °C | *** 11357-3 |
CLTE - Flow (23 to 55°C) | 0.00010 | -- | cm/cm/°C | *** 11359-2 |
CLTE - Transverse (23 to 55°C) | 0.00011 | -- | cm/cm/°C | *** 11359-2 |
RTI Elec (1.50 mm) | 105 | -- | °C | UL 746 |
RTI Imp (1.50 mm) | 65.0 | -- | °C | UL 746 |
RTI Str (1.50 mm) | 75.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | 1.0E+14 | 1.0E+13 | ohm | IEC 60093 |
Volume Resistivity | 1.0E+15 | 1.0E+12 | ohm·cm | IEC 60093 |
Electric Strength | IEC 60243-1 | |||
23°C, 1.00 mm | 30 | 30 | kV/mm | |
23°C, 3.00 mm | 30 | 35 | kV/mm | |
Dielectric Constant 7 | IEC 60250 | |||
50 Hz | 3.80 | 20.0 | ||
23°C, 1 MHz | 3.40 | 4.60 | ||
Relative Permittivity | IEC 60250 | |||
23°C, 100 Hz | 4.00 | 15.0 | ||
23°C, 1 MHz | 3.50 | 4.00 | ||
Dissipation Factor | IEC 60250 | |||
23°C, 100 Hz | 0.017 | 0.20 | ||
23°C, 1 MHz | 0.020 | 0.12 | ||
Comparative Tracking Index | -- | 600 | V | ASTM D3638 |
Comparative Tracking Index | IEC 60112 | |||
Solution A | 600 | -- | V | |
Solution B | 600 | -- | V | |
| Flammability | Dry | Conditioned | Unit | Test Method |
Flame Rating | UL 94 | |||
1.50 mm | V-2 | -- | ||
1.60 mm | V-2 | -- | ||
3.00 mm | V-2 | -- | ||
3.20 mm | V-2 | -- |
订购说明
★公司秉承“以诚为本，信誉至上”的经营宗旨，【诚信***】【服务***】【品质***】创立了自己的经营理念，在客户群树立了良好的***。为您提供充足的货源和专业的技术支持！公司所售之新料均***原厂原包，货真价实!
★公司货源充足，品种齐全，价格合理,量大从优,原厂原包,当天订货当天发货。我公司可以提供原料出厂报告(COA)，认证报告;UL认证、FDA认证、材质证明、***，ASTM物性资料、ROHS(SGS)报告、物质安全资料表(MSDS)物性、报价、UL报告、RoSH标准、SGS检测报告等）......
★支持物流，快递和货运; 支持现金，银行转账（广东省内可快递代收）.
★原料到厂后，请不要拆外包装，应先仔细检查原料的外包装是否完好及原料型号是否与您所订购原料型号相匹配。
★货物送达后，请***时间检查，发现物流过程中出现大量包装损坏及原料外漏的,请让物流人员出具证明并保存，并在24小时内与东莞佳唯斯塑胶原料有限公司颜小姐联系。
★如发货后未能及时收到，请及时与东莞佳唯斯塑胶原料有限公司颜小姐联系15382847379
★订购说明：自接到订单24小时内发货，广州市 深圳市 珠海市 汕头市 韶关市 河源市 梅州市 惠州市 汕尾市 东莞市 中山市 江门市 佛山市 阳江市 湛江市 茂名市 肇庆市 清远市 潮州市 揭阳市 云浮市等地区送货上门，广东省以外等地区协商物流配送，一次购买数量1000kg以上价格从优，欢迎各界朋友前来订购。
★我们的宗旨：【以优惠的价格给广大客户提供优质的品质。本公司货源充足，品种齐全，价格合理】